Keywords
- - (2)
- Molecular dynamics simulation (1)
- PHMB (1)
- Poly(hexamethylene)biguanide (1)
- RNS (1)
- ROS (1)
- Rose Bengal staining (1)
- Ti6Al4V (1)
- TiO2 (1)
- antimicrobial coating (1)
Institute
Publisher
- MDPI (2)
The loss of skin integrity is inevitable in life. Wound healing is a necessary sequence of events to reconstitute the body’s integrity against potentially harmful environmental agents and restore homeostasis. Attempts to improve cutaneous wound healing are therefore as old as humanity itself. Furthermore, nowadays, targeting defective wound healing is of utmost importance in an aging society with underlying diseases such as diabetes and vascular insufficiencies being on the rise. Because chronic wounds’ etiology and specific traits differ, there is widespread polypragmasia in targeting non-healing conditions. Reactive oxygen and nitrogen species (ROS/RNS) are an overarching theme accompanying wound healing and its biological stages. ROS are signaling agents generated by phagocytes to inactivate pathogens. Although ROS/RNS’s central role in the biology of wound healing has long been appreciated, it was only until the recent decade that these agents were explicitly used to target defective wound healing using gas plasma technology. Gas plasma is a physical state of matter and is a partially ionized gas operated at body temperature which generates a plethora of ROS/RNS simultaneously in a spatiotemporally controlled manner. Animal models of wound healing have been vital in driving the development of these wound healing-promoting technologies, and this review summarizes the current knowledge and identifies open ends derived from in vivo wound models under gas plasma therapy. While gas plasma-assisted wound healing in humans has become well established in Europe, veterinary medicine is an emerging field with great potential to improve the lives of suffering animals.
Unlike the native surface of the implant material (Ti6Al4V), oxidation with H2O2 leads to increased binding of the effective antimicrobial agent poly(hexamethylene) biguanide [PHMB]. However, treating with NaOH instead results in an even higher PHMB mass coverage. After oxidation with H2O2, strong differences in the PHMB adsorption capability between polished and corundum-blasted surfaces appear, indicating a roughness dependence. After NaOH treatment, no such effect was observed. The wetting properties of specimens treated with either H2O2 or NaOH prior to PHMB exposure clearly varied. To unravel the nature of this interaction, widespread in silico and in vitro experiments were performed. Methods: By X-ray photoelectron spectroscopy, scanning electron microscopy, water contact angle measurements and MD simulations, we characterized the interplay between the polycationic antimicrobial agent and the implant surface. A theoretical model for PHMB micelles is tested for its wetting properties and compared to carbon contaminated TiO2. In addition, quantitation of anionic functional group equivalents, the binding properties of PHMB with blocked amino end-group, and the ability to bind chlorhexidine digluconate (CHG) were investigated. Ultimately, the capability of osteoblasts to build calcium apatite, and the activity of alkaline phosphatase on PHMB coated specimens, were determined. Results: Simulated water contact angles on carbon contaminated TiO2 surfaces and PHMB micelle models reveal little influence of PHMB on the wetting properties and point out the major influence of remaining and recovering contamination from ambient air. Testing PHMB adsorption beyond the critical micelle concentration and subsequent staining reveals an island-like pattern with H2O2 as compared to an evenly modified surface with NaOH. Both CHG and PHMB, with blocked amino end groups, were adsorbed on the treated surfaces, thus negating the significant influence of PHMB’s terminal groups. The ability of osteoblasts to produce calcium apatite and alkaline phosphatase is not negatively impaired for PHMB mass coverages up to 8 μg/specimen. Conclusion: Differences in PHMB adsorption are triggered by the number of anionic groups and carbon contaminants, both of which depend on the specimen pre-treatment. With more PHMB covering, the implant surface is protected against the capture of new contamination from the ambient air, thus building a robust antimicrobial and biocompatible surface coating.